Is SS 410 good for electrode.
Anyone used SS type 410? What are your experiences with it?
The description says not to be used in corrosive environments?
-
Stainless steels in the 400 group are called Martensitic and are very prone to hydrogen embrittlement (http://en.wikipedia.org/wiki/Hydrogen_embrittlement). Any hardened metals with hardness greater than 30 HRC are prone to hydrogen brittleness. 410 stainless has a hardness of 38-45 HRC (http://www.alleghenyludlum.com/ludlu...oductLine.html).