I am building a hho generator and am wondering if anyone knows how to passivate aluminum plates
I am building a hho generator and am wondering if anyone knows how to passivate aluminum plates
I have used aluminum in the past and it did corode. I was thinking passivation and a different electrolyte would reduce corosion. I am also thinking about using stainless steel if I can avoid hxachrome.
does anyone have an answer?
If you wish to avoid hexachrome then keep your amperage at or below 1/4A per sq. in. and your voltage no higher than ~2.2V per cell and you should be fine. Or just use Nickel201..
[SIGPIC][/SIGPIC]
Thanks! I will remember that.
John, what are you going to use for elite? Iquiring minds want to know.
"D"
I'm not sure and welcome sugestions.
John,
This is just perception and not calculation, but I think that about 2/3 to 3/4 of us use KOH and the remainder use NaOH... Given any more thought to using Nickel200 or 201?
[SIGPIC][/SIGPIC]
Thanks for sugesting KOH. I think thats what I am going to use. And yes my next upgrade will use Nickel if I can find a cheap source.